The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites

3930 Ogledov
4432 Prenosov
Izvoz citacije: ABNT
OZSOY, İskender ;DEMIRKOL, Askin ;MIMAROGLU, Abdullah ;UNAL, Huseyin ;DEMIR, Zafer .
The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites. 
Strojniški vestnik - Journal of Mechanical Engineering, [S.l.], v. 61, n.10, p. 601-609, june 2018. 
ISSN 0039-2480.
Available at: <https://www.sv-jme.eu/sl/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/>. Date accessed: 09 dec. 2024. 
doi:http://dx.doi.org/10.5545/sv-jme.2015.2632.
Ozsoy, ., Demirkol, A., Mimaroglu, A., Unal, H., & Demir, Z.
(2015).
The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites.
Strojniški vestnik - Journal of Mechanical Engineering, 61(10), 601-609.
doi:http://dx.doi.org/10.5545/sv-jme.2015.2632
@article{sv-jmesv-jme.2015.2632,
	author = {İskender  Ozsoy and Askin  Demirkol and Abdullah  Mimaroglu and Huseyin  Unal and Zafer  Demir},
	title = {The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites},
	journal = {Strojniški vestnik - Journal of Mechanical Engineering},
	volume = {61},
	number = {10},
	year = {2015},
	keywords = {micro-filler; nano-filler; mechanical properties; epoxy; composite},
	abstract = {In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio.},
	issn = {0039-2480},	pages = {601-609},	doi = {10.5545/sv-jme.2015.2632},
	url = {https://www.sv-jme.eu/sl/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/}
}
Ozsoy, .,Demirkol, A.,Mimaroglu, A.,Unal, H.,Demir, Z.
2015 June 61. The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites. Strojniški vestnik - Journal of Mechanical Engineering. [Online] 61:10
%A Ozsoy, İskender 
%A Demirkol, Askin 
%A Mimaroglu, Abdullah 
%A Unal, Huseyin 
%A Demir, Zafer 
%D 2015
%T The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites
%B 2015
%9 micro-filler; nano-filler; mechanical properties; epoxy; composite
%! The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites
%K micro-filler; nano-filler; mechanical properties; epoxy; composite
%X In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio.
%U https://www.sv-jme.eu/sl/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/
%0 Journal Article
%R 10.5545/sv-jme.2015.2632
%& 601
%P 9
%J Strojniški vestnik - Journal of Mechanical Engineering
%V 61
%N 10
%@ 0039-2480
%8 2018-06-27
%7 2018-06-27
Ozsoy, İskender, Askin  Demirkol, Abdullah  Mimaroglu, Huseyin  Unal, & Zafer  Demir.
"The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites." Strojniški vestnik - Journal of Mechanical Engineering [Online], 61.10 (2015): 601-609. Web.  09 Dec. 2024
TY  - JOUR
AU  - Ozsoy, İskender 
AU  - Demirkol, Askin 
AU  - Mimaroglu, Abdullah 
AU  - Unal, Huseyin 
AU  - Demir, Zafer 
PY  - 2015
TI  - The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites
JF  - Strojniški vestnik - Journal of Mechanical Engineering
DO  - 10.5545/sv-jme.2015.2632
KW  - micro-filler; nano-filler; mechanical properties; epoxy; composite
N2  - In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio.
UR  - https://www.sv-jme.eu/sl/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/
@article{{sv-jme}{sv-jme.2015.2632},
	author = {Ozsoy, ., Demirkol, A., Mimaroglu, A., Unal, H., Demir, Z.},
	title = {The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites},
	journal = {Strojniški vestnik - Journal of Mechanical Engineering},
	volume = {61},
	number = {10},
	year = {2015},
	doi = {10.5545/sv-jme.2015.2632},
	url = {https://www.sv-jme.eu/sl/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/}
}
TY  - JOUR
AU  - Ozsoy, İskender 
AU  - Demirkol, Askin 
AU  - Mimaroglu, Abdullah 
AU  - Unal, Huseyin 
AU  - Demir, Zafer 
PY  - 2018/06/27
TI  - The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites
JF  - Strojniški vestnik - Journal of Mechanical Engineering; Vol 61, No 10 (2015): Strojniški vestnik - Journal of Mechanical Engineering
DO  - 10.5545/sv-jme.2015.2632
KW  - micro-filler, nano-filler, mechanical properties, epoxy, composite
N2  - In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio.
UR  - https://www.sv-jme.eu/sl/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/
Ozsoy, İskender, Demirkol, Askin, Mimaroglu, Abdullah, Unal, Huseyin, AND Demir, Zafer.
"The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites" Strojniški vestnik - Journal of Mechanical Engineering [Online], Volume 61 Number 10 (27 June 2018)

Avtorji

Inštitucije

  • Sakarya University, Faculty of Engineering, Turkey 1
  • Sakarya University, Faculty of Technology, Turkey 2
  • University of Anadolu, Porsuk High School, Turkey 3

Informacije o papirju

Strojniški vestnik - Journal of Mechanical Engineering 61(2015)10, 601-609
© The Authors, CC-BY 4.0 Int. Change in copyright policy from 2022, Jan 1st.

https://doi.org/10.5545/sv-jme.2015.2632

In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio.

micro-filler; nano-filler; mechanical properties; epoxy; composite