OZSOY, İskender ;DEMIRKOL, Askin ;MIMAROGLU, Abdullah ;UNAL, Huseyin ;DEMIR, Zafer . The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites. Strojniški vestnik - Journal of Mechanical Engineering, [S.l.], v. 61, n.10, p. 601-609, june 2018. ISSN 0039-2480. Available at: <https://www.sv-jme.eu/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/>. Date accessed: 25 apr. 2024. doi:http://dx.doi.org/10.5545/sv-jme.2015.2632.
Ozsoy, ., Demirkol, A., Mimaroglu, A., Unal, H., & Demir, Z. (2015). The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites. Strojniški vestnik - Journal of Mechanical Engineering, 61(10), 601-609. doi:http://dx.doi.org/10.5545/sv-jme.2015.2632
@article{sv-jmesv-jme.2015.2632,
author = {İskender Ozsoy and Askin Demirkol and Abdullah Mimaroglu and Huseyin Unal and Zafer Demir},
title = {The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites},
journal = {Strojniški vestnik - Journal of Mechanical Engineering},
volume = {61},
number = {10},
year = {2015},
keywords = {micro-filler; nano-filler; mechanical properties; epoxy; composite},
abstract = {In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio.},
issn = {0039-2480}, pages = {601-609}, doi = {10.5545/sv-jme.2015.2632},
url = {https://www.sv-jme.eu/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/}
}
Ozsoy, .,Demirkol, A.,Mimaroglu, A.,Unal, H.,Demir, Z. 2015 June 61. The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites. Strojniški vestnik - Journal of Mechanical Engineering. [Online] 61:10
%A Ozsoy, İskender %A Demirkol, Askin %A Mimaroglu, Abdullah %A Unal, Huseyin %A Demir, Zafer %D 2015 %T The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites %B 2015 %9 micro-filler; nano-filler; mechanical properties; epoxy; composite %! The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites %K micro-filler; nano-filler; mechanical properties; epoxy; composite %X In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio. %U https://www.sv-jme.eu/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/ %0 Journal Article %R 10.5545/sv-jme.2015.2632 %& 601 %P 9 %J Strojniški vestnik - Journal of Mechanical Engineering %V 61 %N 10 %@ 0039-2480 %8 2018-06-27 %7 2018-06-27
Ozsoy, İskender, Askin Demirkol, Abdullah Mimaroglu, Huseyin Unal, & Zafer Demir. "The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites." Strojniški vestnik - Journal of Mechanical Engineering [Online], 61.10 (2015): 601-609. Web. 25 Apr. 2024
TY - JOUR AU - Ozsoy, İskender AU - Demirkol, Askin AU - Mimaroglu, Abdullah AU - Unal, Huseyin AU - Demir, Zafer PY - 2015 TI - The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites JF - Strojniški vestnik - Journal of Mechanical Engineering DO - 10.5545/sv-jme.2015.2632 KW - micro-filler; nano-filler; mechanical properties; epoxy; composite N2 - In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio. UR - https://www.sv-jme.eu/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/
@article{{sv-jme}{sv-jme.2015.2632},
author = {Ozsoy, ., Demirkol, A., Mimaroglu, A., Unal, H., Demir, Z.},
title = {The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites},
journal = {Strojniški vestnik - Journal of Mechanical Engineering},
volume = {61},
number = {10},
year = {2015},
doi = {10.5545/sv-jme.2015.2632},
url = {https://www.sv-jme.eu/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/}
}
TY - JOUR AU - Ozsoy, İskender AU - Demirkol, Askin AU - Mimaroglu, Abdullah AU - Unal, Huseyin AU - Demir, Zafer PY - 2018/06/27 TI - The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites JF - Strojniški vestnik - Journal of Mechanical Engineering; Vol 61, No 10 (2015): Strojniški vestnik - Journal of Mechanical Engineering DO - 10.5545/sv-jme.2015.2632 KW - micro-filler, nano-filler, mechanical properties, epoxy, composite N2 - In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio. UR - https://www.sv-jme.eu/article/the-influence-of-micro-and-nano-filler-content-on-the-mechanical-properties-of-epoxy-composites/
Ozsoy, İskender, Demirkol, Askin, Mimaroglu, Abdullah, Unal, Huseyin, AND Demir, Zafer. "The Influence of Micro- and Nano-Filler Content on the Mechanical Properties of Epoxy Composites" Strojniški vestnik - Journal of Mechanical Engineering [Online], Volume 61 Number 10 (27 June 2018)
Strojniški vestnik - Journal of Mechanical Engineering 61(2015)10, 601-609
© The Authors, CC-BY 4.0 Int. Change in copyright policy from 2022, Jan 1st.
In this study, the influence of micro- and nano-filler content on the mechanical properties of epoxy composites was studied. The matrix material is epoxy; the micro-fillers are Al2O3, TiO2 and fly ash added in 10 to 30 wt% by weight ratio; the nano-fillers are Al2O3, TiO2 and clay added in 2.5 to 10 wt% by weight ratio. Test samples were prepared using an open mould type die. Tensile, three-point bending and hardness tests were carried out. The tensile strength, elastic modulus, elongation at break, flexural strength, flexural modulus, and the hardness of the composite materials were obtained and evaluated. The results show that the tensile strength, flexural strength and elongation at the break values of composites decreased while the tensile modulus and flexural modulus increased with the increasing micro- and nano-filler content ratio.