Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application

2170 Views
1446 Downloads
Export citation: ABNT
RAK, Inoslav ;KOCAK, Mustafa ;PETROVSKI, Blagoj .
Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application. 
Strojniški vestnik - Journal of Mechanical Engineering, [S.l.], v. 40, n.11-12, p. 369-380, november 2017. 
ISSN 0039-2480.
Available at: <https://www.sv-jme.eu/article/fracture-toughness-evaluation-of-repair-welded-joints-for-offshore-application/>. Date accessed: 10 dec. 2024. 
doi:http://dx.doi.org/.
Rak, I., Kocak, M., & Petrovski, B.
(1994).
Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application.
Strojniški vestnik - Journal of Mechanical Engineering, 40(11-12), 369-380.
doi:http://dx.doi.org/
@article{.,
	author = {Inoslav  Rak and Mustafa  Kocak and Blagoj  Petrovski},
	title = {Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application},
	journal = {Strojniški vestnik - Journal of Mechanical Engineering},
	volume = {40},
	number = {11-12},
	year = {1994},
	keywords = {Fracture Toughness; Joints; Offshore Application; },
	abstract = {The crack tip opening displacement (CTOD) toughness evaluation of repaired weld joints (presence of two weld deposits, complex mechanical heterogeneity and high residual stresses) requires some modifications to commonly used specimen geometry and testing procedures. This paper presents the results of single edge bend (SENB) specimens with shallow (a/W = = 0.16) and deep notches (a/W = 0.3 to 0.5) extracted from 30 mm thick multipass submerged arc welded (SAW) joints which had been repaired with a hyperbaric (16 bar) welding process at the toe region of the original SAW weld deposits. The results show that an acceptable toughness level can be achieved for hyperbaric repair weld metals deposited at 16 bar (160 m water depth). The repaired single bevel-joint on 30 mm thick StE 445.7 TM steel contained low toughness heat affected zone (local brittle zone). The CTOD toughness evaluation (according to BS 5762 standard and CTOD (S5) techniques) of both plates contained a series of shallow and deep cracked SENB specimens notched (through thickness and surface) at various locations of the repaired weld joints. The directly measured CTOD (S5) values are consistent with the calculated CTOD BS 5762 values. An effect of weld metal overmatching on through thickness shallow cracked SENB specimen result was observed, since these specimens can produce low CTOD values despite their lower crack tip constraint.},
	issn = {0039-2480},	pages = {369-380},	doi = {},
	url = {https://www.sv-jme.eu/article/fracture-toughness-evaluation-of-repair-welded-joints-for-offshore-application/}
}
Rak, I.,Kocak, M.,Petrovski, B.
1994 November 40. Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application. Strojniški vestnik - Journal of Mechanical Engineering. [Online] 40:11-12
%A Rak, Inoslav 
%A Kocak, Mustafa 
%A Petrovski, Blagoj 
%D 1994
%T Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application
%B 1994
%9 Fracture Toughness; Joints; Offshore Application; 
%! Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application
%K Fracture Toughness; Joints; Offshore Application; 
%X The crack tip opening displacement (CTOD) toughness evaluation of repaired weld joints (presence of two weld deposits, complex mechanical heterogeneity and high residual stresses) requires some modifications to commonly used specimen geometry and testing procedures. This paper presents the results of single edge bend (SENB) specimens with shallow (a/W = = 0.16) and deep notches (a/W = 0.3 to 0.5) extracted from 30 mm thick multipass submerged arc welded (SAW) joints which had been repaired with a hyperbaric (16 bar) welding process at the toe region of the original SAW weld deposits. The results show that an acceptable toughness level can be achieved for hyperbaric repair weld metals deposited at 16 bar (160 m water depth). The repaired single bevel-joint on 30 mm thick StE 445.7 TM steel contained low toughness heat affected zone (local brittle zone). The CTOD toughness evaluation (according to BS 5762 standard and CTOD (S5) techniques) of both plates contained a series of shallow and deep cracked SENB specimens notched (through thickness and surface) at various locations of the repaired weld joints. The directly measured CTOD (S5) values are consistent with the calculated CTOD BS 5762 values. An effect of weld metal overmatching on through thickness shallow cracked SENB specimen result was observed, since these specimens can produce low CTOD values despite their lower crack tip constraint.
%U https://www.sv-jme.eu/article/fracture-toughness-evaluation-of-repair-welded-joints-for-offshore-application/
%0 Journal Article
%R 
%& 369
%P 12
%J Strojniški vestnik - Journal of Mechanical Engineering
%V 40
%N 11-12
%@ 0039-2480
%8 2017-11-11
%7 2017-11-11
Rak, Inoslav, Mustafa  Kocak, & Blagoj  Petrovski.
"Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application." Strojniški vestnik - Journal of Mechanical Engineering [Online], 40.11-12 (1994): 369-380. Web.  10 Dec. 2024
TY  - JOUR
AU  - Rak, Inoslav 
AU  - Kocak, Mustafa 
AU  - Petrovski, Blagoj 
PY  - 1994
TI  - Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application
JF  - Strojniški vestnik - Journal of Mechanical Engineering
DO  - 
KW  - Fracture Toughness; Joints; Offshore Application; 
N2  - The crack tip opening displacement (CTOD) toughness evaluation of repaired weld joints (presence of two weld deposits, complex mechanical heterogeneity and high residual stresses) requires some modifications to commonly used specimen geometry and testing procedures. This paper presents the results of single edge bend (SENB) specimens with shallow (a/W = = 0.16) and deep notches (a/W = 0.3 to 0.5) extracted from 30 mm thick multipass submerged arc welded (SAW) joints which had been repaired with a hyperbaric (16 bar) welding process at the toe region of the original SAW weld deposits. The results show that an acceptable toughness level can be achieved for hyperbaric repair weld metals deposited at 16 bar (160 m water depth). The repaired single bevel-joint on 30 mm thick StE 445.7 TM steel contained low toughness heat affected zone (local brittle zone). The CTOD toughness evaluation (according to BS 5762 standard and CTOD (S5) techniques) of both plates contained a series of shallow and deep cracked SENB specimens notched (through thickness and surface) at various locations of the repaired weld joints. The directly measured CTOD (S5) values are consistent with the calculated CTOD BS 5762 values. An effect of weld metal overmatching on through thickness shallow cracked SENB specimen result was observed, since these specimens can produce low CTOD values despite their lower crack tip constraint.
UR  - https://www.sv-jme.eu/article/fracture-toughness-evaluation-of-repair-welded-joints-for-offshore-application/
@article{{}{.},
	author = {Rak, I., Kocak, M., Petrovski, B.},
	title = {Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application},
	journal = {Strojniški vestnik - Journal of Mechanical Engineering},
	volume = {40},
	number = {11-12},
	year = {1994},
	doi = {},
	url = {https://www.sv-jme.eu/article/fracture-toughness-evaluation-of-repair-welded-joints-for-offshore-application/}
}
TY  - JOUR
AU  - Rak, Inoslav 
AU  - Kocak, Mustafa 
AU  - Petrovski, Blagoj 
PY  - 2017/11/11
TI  - Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application
JF  - Strojniški vestnik - Journal of Mechanical Engineering; Vol 40, No 11-12 (1994): Strojniški vestnik - Journal of Mechanical Engineering
DO  - 
KW  - Fracture Toughness, Joints, Offshore Application, 
N2  - The crack tip opening displacement (CTOD) toughness evaluation of repaired weld joints (presence of two weld deposits, complex mechanical heterogeneity and high residual stresses) requires some modifications to commonly used specimen geometry and testing procedures. This paper presents the results of single edge bend (SENB) specimens with shallow (a/W = = 0.16) and deep notches (a/W = 0.3 to 0.5) extracted from 30 mm thick multipass submerged arc welded (SAW) joints which had been repaired with a hyperbaric (16 bar) welding process at the toe region of the original SAW weld deposits. The results show that an acceptable toughness level can be achieved for hyperbaric repair weld metals deposited at 16 bar (160 m water depth). The repaired single bevel-joint on 30 mm thick StE 445.7 TM steel contained low toughness heat affected zone (local brittle zone). The CTOD toughness evaluation (according to BS 5762 standard and CTOD (S5) techniques) of both plates contained a series of shallow and deep cracked SENB specimens notched (through thickness and surface) at various locations of the repaired weld joints. The directly measured CTOD (S5) values are consistent with the calculated CTOD BS 5762 values. An effect of weld metal overmatching on through thickness shallow cracked SENB specimen result was observed, since these specimens can produce low CTOD values despite their lower crack tip constraint.
UR  - https://www.sv-jme.eu/article/fracture-toughness-evaluation-of-repair-welded-joints-for-offshore-application/
Rak, Inoslav, Kocak, Mustafa, AND Petrovski, Blagoj.
"Fracture Toughness Evaluation of Repair Welded Joints for Offshore Application" Strojniški vestnik - Journal of Mechanical Engineering [Online], Volume 40 Number 11-12 (11 November 2017)

Authors

Affiliations

  • Faculty of Engineering, Maribor, Slovenia
  • GKSS Research Center, Germany
  • GKSS Research Center, Germany

Paper's information

Strojniški vestnik - Journal of Mechanical Engineering 40(1994)11-12, 369-380
© The Authors, CC-BY 4.0 Int. Change in copyright policy from 2022, Jan 1st.

The crack tip opening displacement (CTOD) toughness evaluation of repaired weld joints (presence of two weld deposits, complex mechanical heterogeneity and high residual stresses) requires some modifications to commonly used specimen geometry and testing procedures. This paper presents the results of single edge bend (SENB) specimens with shallow (a/W = = 0.16) and deep notches (a/W = 0.3 to 0.5) extracted from 30 mm thick multipass submerged arc welded (SAW) joints which had been repaired with a hyperbaric (16 bar) welding process at the toe region of the original SAW weld deposits. The results show that an acceptable toughness level can be achieved for hyperbaric repair weld metals deposited at 16 bar (160 m water depth). The repaired single bevel-joint on 30 mm thick StE 445.7 TM steel contained low toughness heat affected zone (local brittle zone). The CTOD toughness evaluation (according to BS 5762 standard and CTOD (S5) techniques) of both plates contained a series of shallow and deep cracked SENB specimens notched (through thickness and surface) at various locations of the repaired weld joints. The directly measured CTOD (S5) values are consistent with the calculated CTOD BS 5762 values. An effect of weld metal overmatching on through thickness shallow cracked SENB specimen result was observed, since these specimens can produce low CTOD values despite their lower crack tip constraint.

Fracture Toughness; Joints; Offshore Application;